There are many different types of surface finish on stainless steel. Some of these originate from the mill but many are applied later during processing, for example polished, brushed, blasted, etched and coloured finishes.
The importance of surface finish in determining the corrosion resistance of the stainless steel surface cannot be overemphasised. A rough surface finish can effectively lower the corrosion resistance to that of a lower grade of stainless steel.
The European standards for stainless steels have attempted to define the most common surface finishes. However, due to the proprietary nature of many suppliers’ finishes, it is unlikely that complete standardisation is possible. This is a summary of the most common types for each product form
Common Surface Finishes for Stainless Steel Flat Products from EN 10088-2 (for full list see Specifying finishes for stainless steel flat products (sheet and plate)
Surface Finish Code
Description
Mill finishes
1D
Hot rolled, heat treated, pickled. The most common hot rolled finish. A non reflective, rough surface.
Not normally used for decorative applications
2B
Cold rolled, heat treated, pickled, pinch passed. The most common cold rolled mill finish. Dull grey slightly reflective finish.
Can be used in this condition or frequently is the starting point for a wide range of polished finishes.
2D
Cold rolled, heat treated, pickled.
2H
Work hardened by rolling to give enhanced strength level. Various ranges of tensile or 0.2% proof strength are given in
EN 10088-2 up to 1300 MPa and 1100 MPa respectively dependent on grade
2Q
Cold rolled hardened and tempered. Applies to martensitic steels which respond to this kind of heat treatment.
2R
Cold rolled and bright annealed, still commonly known as BA. A bright reflective finish. Can be used in this condition or
as the starting point for polishing or other surface treatment processes e.g. colouring
In the following codes “1” refers to hot rolled being the starting point and “2” as cold rolled
Special Finishes
1G or 2G
Ground. Relatively coarse surface. Unidirectional. Grade of polishing grit or surface roughness can be specified
1J or 2J
Brushed or dull polished. Smoother than 1G/2G. Grade of polishing grit or surface roughness can be specified
1K or 2K
Satin polish. Similar to 1J/2J but with maximum specified Ra value of 0.5 micron. Usually achieved with SiC polishing belts.
Alumina belts are strongly discouraged for this finish as this will have detrimental effect on corrosion resistance.
Recommended for external architectural and coastal environments where bright polish (1P/2P) is not acceptable.
1P/2P
Bright polished. Non-directional, reflective. Can specify maximum surface roughness. The best surface for corrosion resistance.
2L
Coloured by chemical process to thicken the passive layer and produce interference colours. A wide range of colours is possible.
1M/2M
Patterned. One surface flat.
1S/2S
Surface coated e.g. with tin = Terne coating
2W
Corrugated. Similar to patterned but both surfaces are affected
Bead blastingNot in EN 10088-2. Work being undertaken to more accurately define finishes.
Established in 2008, wilsonpipeline Pipe Industry Co., Limited is a professional organizer and one-stop-shop supplier for stainless steel piping system products, including stainless steel pipes and stainless steel tubes, stainless steel forged flanges and butt-welding stainless steel pipe fittings, stainless steel pipe fittings, stainless steel elbows, stainless steel tees, stainless steel reducer, stainless steel stub end, stainless steel gaskets, stainless steel fasteners, stainless steel valves, Sanitary Services, stainless steel bar, etc. in China. We have devoted to providing the best solutions of steel materials and industrial equipment for our respected customers.
We supply not only commonly used stainless steel materials (SS304/L,SS316/L,SS321), but also duplex and super duplex steel 1.4547, 1.4462, 1.4410 (S31254,S31803,S32750,S32760), special austenite stainless 310S, 347H, 347, 317L, 904L… wilsonpipeline products are widely used in Shipbuilding, Nuclear power, Marine engineering, Petroleum, Chemical, Mining,Sewage treatment, Natural gas and Pressure vessels and other industries.
Source: wilsonpipeline Pipe Industry (www.wilsonpipeline.com)
Comments