Stainless steel 410 is a basic martensitic grade which contains 11.5% chromium, offering both exceptional wear and corrosion resistance. Stainless steel 410 is corrosion resistant to some chemicals, food, mild acids, water, and air. It also proves adequate resistance to nitric acid, concentrated sulfuric acid, dilute acetic acid and naphtha. Elevated mechanical properties and corrosion resistance are achieved with stainless steel 410 when it’s hardened and tempered.
Stainless steel 410 is used in applications such as dental and surgical instruments, pipelines, valves and nozzles, automotive parts and more.Stainless steel 410 is generally used for applications which involve mild corrosion, high strength, and heat resistance. Please contact wilsonpipeline Pipe Industry for more information about stainless steel 410, its properties, and its applications.
Heat Treatment:
Galvanizing: Heat slowly to 1500 -1650°F, cool to 1100°F in furnace, air cool. Process Galvanizing: Heat to 1350 -1450°F, air cool. Hardening: Heat to 1700 – 1850°F, air cool or oil quench. Follow by temper or stress-relief. Stress Relieving: Heat at 300 – 800°F for 1 to 2 hours, air cool. See our stainless steel heat treating services.
Forming:
Stainless steel 410 has cold working properties which allow it to be temperately drawn and shaped in the galvanized condition.
Fabrication:
The martensitic alloys offer unique hardening capabilities which limit their capability of being welded using conventional techniques. Stainless steel 410must first be pre-heated, followed by a post-weld galvanizing treatment to alleviate cracking.
Stainless steel 410 Standards
UNS S41000
ASTM A182
ASTM A276
ASTM A479
Composition (%)
Carbon 0.080-0.150
Chromium 11.50-13.50
Manganese 1.0 Max
Phosphorus 1.0 Max
Silicon 1.00 Max
Sulfur 0.030 Max
Applications
Pump Shafts
Valve Components
Gas and Steam Turbine Components
Blind Flanges
Lap Joint Flanges
Weld Neck Flanges
Slip On Flanges
Plate Flanges
Stainless Steel 410 Pipes Stock
Welded Steel Pipes
Heat Exchanger Tubes
ERW Pipes
Cold Draw Seamless Pipes
Stainless Steel 410 Pipe Fittings Stock
Butt Welding Fittings
Forged Fittingss
Equal Tee
Reducing Tee
Stainless Steel 410 Mechanical PropertiesMaterial TypeConditionUltimate Tensile Strength (PSI)0.2% Yield Strength (PSI)Elongation (% In 2in.)Reduction Of Area (%)Hardness BrinellHardness RockwellStainless steel 410 T100,00080,0001240** H120,00090,0001240** Annealed70,00040,0001645** Class2110,00085,0001545269 Max* NACE MRO 175*****22 HRC Max
Our website: www.wilsonpipeline.com . Please send your detailed requirements to sales@wilsonpipeline.com. We will give you the best offer.