Duplex UNS 31803

SPECIFICATIONS: GRADE Duplex | UNS S31803 | ASTM/ASME A240 / F51 | Werkstoff 1.4462

Zhejiang wilsonpipeline Pipe Industry Co., Limited is a professional organizer and one-stop-shop supplier for special steel, duplex steel, duplex stainless steel flangessuper duplex stainless steel flangesstainless steel flangesStainless Steel Pipesstainless steel pipe fittings etc.


The following are the properties of 31803:

  1. Stainless ferritic-austenitic Cr-Ni-Mo steel with nitrogen addition.

  2. High corrosion resistance, especially against stress corrosion cracking in solutions containing chloride.

  3. Good strength properties.

  4. Resistant to intergranular corrosion in the temperature range up to 300°C.

  5. Heat treatment subsequent to welding not necessary.

  6. Surface condition for optimum corrosion resistance: pickled, heat treated free from scale or machined.

Application

Components in the chemical industry, e.g. separator and heat exchanger parts, from the paper industry, oil and gas production, compressor parts, seawater desalination plants.


Chemical Composition (average %)CSiMnCrMoNiN0.0250.601.3022.603.205.800.17

StandardsEN / DINASTMUNSAFNOR<1.4462 > X2CrNiMoN22-5-3A240S31803Z2CND22-5 Az

Hot Forming

Forging

1200 to 950°C / Air cooling

Heat Treatment

Solution annealing:

1020 to 1100°C Water , air (thickness below 2mm)

Structure

Ferrite + Austenite


Condition: solution annealedProductDimension Size mm0.2% proof stress N/mm2 min.Tensile strength N/mm2Elongation A5 % min. L    Q     TImpact strength (ISO-V) J min. L    Q     TSt≤ 160450650 – 88025   – –    – –100   – –    – –Bl≤ 75460640 – 840252)  252)  – –90   60    – –

St = Bar , Bl = Sheet or plate L = Longitudinal, Q = Transverse, T = Tangential 1) For sheet or plate < 3mm = A80mm specimen The values for other products and dimensions shall be established by agreement.


Condition: solution annealed0.2% proof stress N/mm2 min.Temperature100°C150°C200°C250°C360335315300

Welding

Good weldability. Welding is possible with all processes usual for stainless steels. We recommend depending on applications electric arc welding with covered electrodes, inert gas welding or SA-welding. Preheating and heat treatment after welding is not necessary. For high stressed heavy walled constructions the limited preheat temperature of 150°C maximum is recommendable. Maximum interpass temperature 150°C. Keep heat input low especially for small wall thicknesses. The TIG-process should be given reference for root welding.


Thermal conductivity at ……………….. 20°C ………………15.0 ………W/(m.K) Specific heat at …………………………..20°C ………………500 ……….J/(kg.K) Electrical resistivity at …………………. 20°C ………………0.80 ………Ohm.mm2/m Modulus of elasticity at ……………….. 20°C ………………200 x 103 N/mm2 Magnetic properties ……………………………………………..magneticThermal expansion between 20°C and …°C, 10-6 m/(m.K) atTemperature10-6 m/(m.K)100°C13.0200°C13.5300°C14.0Modulus of elasticity, 103 N/mm2 atTemperature103 N/mm220°C200100°C194200°C186300°C180

As regards applications and processing steps that are not expressly mentioned in this product description/data sheet, the customer shall in each inpidual case be required to consult us.

2 views0 comments

Recent Posts

See All

Knowledge About Steel Elbow

Elbows 45° - 90° - 180° LR/SR The function of a elbow is to change direction or flow in a piping system. By default, there are 5...

Knowledge About Buttweld Fittings

Buttweld Fittings general A pipe fitting is defined as a part used in a piping system, for changing direction, branching or for change of...

List of Chemical Elements

Flange Fittings&Pipes origin supplier from china Wilson Pipeline WhatsApp+8618632758880 sales@wilsonpipeline.com www.wilsonpipeline.com

Comments


bottom of page