317L Stainless Steel Description
Type 317L Stainless Steel (UNS 31703) is a low carbon austenitic chromium-nickel stainless steel that can be used in applications where it is not possible to anneal after welding and where maximum corrosion resistance is required. It provides good oxidation resistance in intermittent service to 1600°F and in continuous service to 1700°F.
Chemistry Typical
Carbon: 0.030 max Manganese: 2.00 max Silicon: 0.75 max Chromium: 18.00-20.00 Nickel: 11.00-15.00 Molybdenum: 3.00-4.00 Phosphorus: 0.045 max
Iron: Balance
Physical Properties
Density 0.29 lbs/in3,7.99 g/cm3
Electrical Resistivity, microhm-in (microhm-cm):
68°F (20°C): 31.19 (79.0)
Specific Heat: BTU/lb/°F (kJ/kg•K):
32-212°F (0-100°C): 0.12 (0.50)
Thermal Conductivity: BTU/hr/ft2/ft/°F (W/m•K)
At 212°F (100°C): 9.4 (16.2)
At 932°F (500C): 12.4 (21.4)
Mean Coefficient of Thermal Expansion:in/in/°F (μm/m•K) 32 – 212°F (0 -100°C): 8.9 x 10-6(16.0) 32 – 600°F (0 -315°C): 9.0 x 10-6(16.2) 32 -1000°F (0 -538°C): 9.7 x 10-6 (17.5) 32 -1200°F (0 -649°C): 10.3 x 10-6 (18.5) 32 -1500ºF (0 -871ºC): 11.1 x 10-6 (18.5)
Modulus of Elasticity: ksi (MPa) 28.0 x 103 (193 x 103) in tension 11.2 x 103 (77 x 103) in torsion
Magnetic Permeability: H = 200 Oersteds: Annealed < 1.02 max.
Creep Strength: 1% Flow in 10,000hrs. At 1000°F : 24,000psi
Melting Range: °F (°C) 2500 – 2590 (1371 – 1421)
Forms
Stainless Steel Flanges – Slip on flanges, Blind flanges, Lap joint flanges, Welding neck flanges, Spectacle flanges, TG flanges, Socket welding flanges and Threaded flanges, Square flanges. Stainless Steel Pipe Fittings – Butt Welding Fittings, Forged Fittings, 180 Degree Elbows, 90 Degree Elbows, 45 Degree Elbows, 30 Degree Elbows, Equal Tee, Reducing Tee, Concentric Reducer, Eccentric Reducer, Lap Joint Stub End, Cap, Cross. Stainless Steel Pipes.
Mechanical Properties at Room Temperature
Properties: Annealed Ultimate Tensile Strength: 75 KSI min (515 MPa min) Yield Strength: (0.2% Offset) 30 KSI min (205 MPa min) Elongation: 35% min Hardness: Rb 95 max
Properties: Tempered Type 317L Stainless Steel can be cold rolled to tempers. Contact Ulbrich Technical Services for more details.
AdditonalProperties
Corrosion Resistance See NACE (National Association of Corrosion Engineers) for recommendations.
Finishes
# 1 –Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required. # 2D – Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process. # 2B –Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D. #BA Bright annealed cold rolled and bright annealed #CBA Course bright annealed cold rolled matte finish and bright anneal #2 Cold Rolled # 2BA – Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part. Polished – Various grit finish for specific polish finished requirements
Wire Finishes
XC – Extra clean bright annealed or bright annealed and cold rolled
Grease – Ultra bright finish for decorative applications
Soap – Soap is not removed from tempered wire to act as a lubricant.
Cold Forming Type 317L Stainless Steel can be readily formed and drawn.
Heat Treatment Type 317L Stainless Steel is non hardenable by heat treatment and can only be hardened by cold working.
Welding For best results refer to: SSINA’s “Welding of Stainless Steel and Other Joining Methods”.
Applications
Chemical Processing, Food Processing, Oil Refineries, Paper Mills, Gas Scrubbers, Photographic Handling, and Marine Parts.